The role of the cold end of glass container production is to complete the final tasks in the manufacturing process: spray on a polyethylene coating for abrasion resistance and increased lubricity, inspect the containers for defects, label the containers, and package the containers for shipment.
The Fourcault process is a method of manufacturing plate glass. First developed in Belgium by Émile Fourcault (1862–1919) during the early 1900s, the process was used globally. Fourcault is an example of a "vertical draw" process, in that the glass is drawn against gravity in an upward direction. [1] Gravity forces influence parts of the ...
The float glass process is also known as the Pilkington process, named after the British glass manufacturer Pilkington, [4] which pioneered the technique in the 1950s at their production site in St Helens, Merseyside. [5] Modern windows are usually made from float glass, [6] though Corning Incorporated uses the overflow downdraw method. [7]
Until the 20th century, window glass production involved blowing a cylinder and flattening it. [9] Two major methods to make window glass, the crown method and the cylinder method, were used until the process was changed much later in the 1920s. [10] All glass products must then be cooled gradually , or else they could easily break. [11]
Pages in category "Glass production" ... Float glass; Fourcault process; Fusion splicing; G. Glasfabrik Lamberts; Glass (1958 film) Glass bead making; Glass casting;
Machine drawn cylinder sheet was the first mechanical method for "drawing" window glass. Cylinders of glass 40 feet (12 m) high are drawn vertically from a circular tank. The glass is then annealed and cut into 7 to 10 foot (2 to 3 m) cylinders. These are cut lengthways, reheated, and flattened. This process was invented in the US in 1903.
Summary of process Temperature (in °C), travel (in mm), and force (in N) during the process. The precision glass moulding process consists of six steps: [1] [2] The glass blank is loaded into the lower side of the moulding tool. Oxygen is removed from the working area by filling with nitrogen and/or evacuation of the process chamber.
Glass casting is the process in which glass objects are cast by directing molten glass into a mould where it solidifies. The technique has been used since the 15th century BCE in both Ancient Egypt and Mesopotamia. Modern cast glass is formed by a variety of processes such as kiln casting or casting into sand, graphite or metal moulds.