A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels .
A Rockwell hardness tester. The Rockwell hardness test is a hardness test based on indentation hardness of a material. The Rockwell test measures the depth of penetration of an indenter under a large load (major load) compared to the penetration made by a preload (minor load). [1]
Vickers hardness test; Brinell scale This page was last edited on 16 November 2024, at 12:16 (UTC). Text is available under the Creative Commons ...
Brinell hardness is sometimes quoted in megapascals; the Brinell hardness number is multiplied by the acceleration due to gravity, 9.80665 m/s 2, to convert it to megapascals. The Brinell hardness number can be correlated with the ultimate tensile strength (UTS), although the relationship is dependent on the material, and therefore determined ...
Most rockwell testers are unreliable below HRC 20. A graph of Vickers 150kg versus the other scales makes sense. Vickers 150kg scale covers a very large range of hardness. The Mohs scale of hardness is so different from the metals hardness scale, that comparison is difficult. ASTM E18 for rockwell, ASTM E10 for Brinell define the limits of ...
The Vickers hardness test; The Brinell scale; The Janka hardness test; The Rockwell scale; The Durometer scale; The Barcol scale; The Leeb rebound hardness scale;
Brinell hardness test (HB) BHN and HBW are widely used [7] Knoop hardness test (HK), for measurement over small areas, widely used to test glass or ceramic material. [8] Janka hardness test, for wood; Meyer hardness test; Rockwell hardness test (HR), principally used in the USA. HRA, HRB and HRC scales are most widely used.
This is similar to using various indenter geometries and test loads in Rockwell (e.g. HRA, HRB, HRC), Brinell and Vickers. Equotip hardness results in HLx are often converted to the traditional hardness scales HRC, HB and HV mainly for convention reasons between supplier and customer. [5] [6]