The SAE steel grades system is a standard alloy numbering system (SAE J1086 – Numbering Metals and Alloys) for steel grades maintained by SAE International. In the 1930s and 1940s, the American Iron and Steel Institute (AISI) and SAE were both involved in efforts to standardize such a numbering system for steels. These efforts were similar ...
For alloys in general (including steel), unified numbering system (UNS) of ASTM International and the Society of Automotive Engineers (SAE). American steel grades : AISI/SAE steel grades standard; British Standards; International Organization for Standardization ISO/TS 4949:2016; European standards – EN 10027
It has a higher corrosion resistance than regular steel and is widely used because of the ease in which it is formed into various shapes. [1] The composition was developed by W. H. Hatfield at Firth Brown in 1924 and was marketed under the trade name "Staybrite 18/8". [2] It is specified by SAE International as part of its SAE steel grades.
UNS K11547 is T2 tool steel; UNS S17400 is ASTM grade 630, Cr-Ni 17-4PH precipitation hardened stainless steel; UNS S30400 is SAE 304, Cr/Ni 18/10, Euronorm 1.4301 stainless steel; UNS S31600 is SAE 316; UNS S31603 is 316L, a low carbon version of 316. The digits "03" were assigned since the maximum allowed carbon content is 0.03%; UNS C90300 ...
The AISI acronym is commonly seen as a prefix to steel grades, for example, "AISI 4140". The SAE steel grade system was formerly a joint AISI-SAE system. Al or AL: aluminium: ALY: alloy: AMER: American: Referring to the United States: AMS: Aerospace Material Standards
300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless steel is Type 304, also known as 18/8 or A2. Type 304 is extensively used in such items as cookware, cutlery, and kitchen equipment. Type 316, also known as A4, is the next most common austenitic stainless steel.
Ferritic stainless steel alloys are designated as part of the 400-series of stainless steels in the SAE steel grades numbering system. By comparison with austenitic stainless steels, these are less hardenable by cold working and less weldable, but more cost-effective due to the lower nickel content.
Duplex steels also have higher strength. For example, a Type 304 stainless steel has a 0.2% proof strength in the region of 280 MPa (41 ksi), a 22%Cr duplex stainless steel a minimum 0.2% proof strength of some 450 MPa (65 ksi) and a superduplex grade a minimum of 550 MPa (80 ksi). [6]