Density system unit unit-code symbol or abbrev. notes sample default conversion combination output units Metric: kilogram per cubic metre: kg/m3 kg/m 3: 1.0 kg/m 3 (1.7 lb/cu yd)
HDPE is known for its high strength-to-density ratio. [4] The density of HDPE ranges from 930 to 970 kg/m 3. [5] Although the density of HDPE is only marginally higher than that of low-density polyethylene, HDPE has little branching, giving it stronger intermolecular forces and tensile strength (38 MPa versus 21 MPa) than LDPE. [6]
— "Values ranging from 21.3 to 21.5 gm/cm 3 at 20 °C have been reported for the density of annealed platinum; the best value being about 21.45 gm/cm 3 at 20 °C." 21.46 g/cm 3 — Rose, T. Kirke. The Precious Metals, Comprising Gold, Silver and Platinum .
The high molecular weight makes it a very tough material, but results in less efficient packing of the chains into the crystal structure as evidenced by densities of less than high-density polyethylene (for example, 0.930–0.935 g/cm 3). UHMWPE can be made through any catalyst technology, although Ziegler catalysts are most common.
A typical 11 mm (0.43 in) UHMWPE rope of 30 m (98 ft) can weigh around 2 kg (4.4 lb), the equivalent steel wire rope would weigh around 13 kg (29 lb). One notable drawback of UHMWPE rope is its susceptibility to UV damage, so many users will fit winch covers in order to protect the cable when not in use.
The standard unit is the meter cubed per kilogram (m 3 /kg or m 3 ·kg −1). Sometimes specific volume is expressed in terms of the number of cubic centimeters occupied by one gram of a substance. In this case, the unit is the centimeter cubed per gram (cm 3 /g or cm 3 ·g −1). To convert m 3 /kg to cm 3 /g, multiply by 1000; conversely ...
The SI unit of kilogram per cubic metre (kg/m 3) and the cgs unit of gram per cubic centimetre (g/cm 3) are probably the most commonly used units for density. One g/cm 3 is equal to 1000 kg/m 3. One cubic centimetre (abbreviation cc) is equal to one millilitre.
EPE foams are low density, semi-rigid, closed cell foam that are generally somewhere in stiffness/compliance between Expanded polystyrene and Polyurethane. Production of EPE foams is similar to that of expanded polystyrene, but starting with PE beads. [1] Typical densities are 29 to 120 kg/m 3 (49 to 202 lb/cu yd) with the lower figure being ...