Wrought iron is an iron alloy with a very low carbon content (less than 0.05%) in contrast to that of cast iron (2.1% to 4.5%). It is a semi-fused mass of iron with fibrous slag inclusions (up to 2% by weight), which give it a wood-like "grain" that is visible when it is etched, rusted, or bent to failure.
While iron is now the name of a chemical element, the traditional meaning of the word "iron" is what is now called wrought iron. In East Asia, cast iron was also common after 500 BCE, and was called "cooked iron", with wrought iron being called "raw iron" (in Europe, cast iron remained very rare until it was used for cannonballs in the 14th ...
Ironwork is any weapon, artwork, utensil, or architectural feature made of iron, especially one used for decoration. There are two main types of ironwork: wrought iron and cast iron. While the use of iron dates as far back as 4000 BC, it was the Hittites who first knew how to extract it (see iron ore) and develop weapons.
Cast iron is made from pig iron, which is the product of melting iron ore in a blast furnace. Cast iron can be made directly from the molten pig iron or by re-melting pig iron, [4] often along with substantial quantities of iron, steel, limestone, carbon (coke) and taking various steps to remove undesirable contaminants.
Cast iron is a brittle form of iron which is weaker in tension than in compression. It has a relatively low melting point, good fluidity, castability, excellent machinability and wear resistance. Though almost entirely replaced by steel in building structures, cast irons have become an engineering material with a wide range of applications ...
Cast iron development lagged in Europe because wrought iron was the desired product and the intermediate step of producing cast iron involved an expensive blast furnace and further refining of pig iron to cast iron, which then required a labor and capital intensive conversion to wrought iron. [11]
Iron treated this way is said to be wrought (worked), and the resulting iron, with reduced amounts of slag, is called wrought iron or bar iron. Because of the creation process, individual blooms can often have differing carbon contents between the original top and bottom surfaces, differences that will also be somewhat blended together through ...
Cast iron is not a good structural material for handling tension or bending moments because of its brittleness and relatively low tensile strength compared to steel and wrought iron. However, cast iron does have good compressive strength and was successfully used for structural components that were largely in compression in well-designed ...