The substrate is then rotated at speeds up to 10,000 rpm to spread the coating material by centrifugal force. A machine used for spin coating is called a spin coater, or simply spinner. [1] Rotation is continued while the fluid spins off the edges of the substrate, until the desired thickness of the film is achieved.
There are four basic parameters that are involved in spin coating: solution viscosity, solid content (density), angular speed, and spin time. [13] A range of thicknesses can be achieved by spin coating. Most commonly the thicknesses range from 1-200 μm. The main properties that affect the thickness of the film are viscosity and spin speed.
Spin casting, also known as centrifugal rubber mold casting (CRMC), is a method of utilizing inertia to produce castings from a rubber mold. Typically, a disc-shaped mold is spun along its central axis at a set speed.
The spin and dip coating methods are simple methods for nanoparticle deposition. [4] They are useful tools especially in creating self-assembled layers and films where the packing density isn't critical. Accurate and vibration-free sample withdrawal speeds can be used to have control over the film thickness.
Spin coating or spin casting, uses a liquid precursor, or sol-gel precursor deposited onto a smooth, flat substrate which is subsequently spun at a high velocity to centrifugally spread the solution over the substrate. The speed at which the solution is spun and the viscosity of the sol determine the ultimate thickness of the deposited film ...
The bilayers and wash steps can be performed in many different ways including dip coating, spin-coating, spray-coating, flow based techniques and electro-magnetic techniques. [1] The preparation method distinctly impacts the properties of the resultant films, allowing various applications to be realized. [ 1 ]
Slot-die coating is a non-contact coating method, in which the slot-die is typically held over the substrate at a height several times higher than the target wet film thickness. [23] The coating fluid transfers from the slot-die to the substrate via a fluid bridge that spans the air gap between the slot-die lips and substrate surface.
The thickness of the metal to be spun can vary from about 0.1 mm (0.004 in) to 120 mm (4 or 5 in) on special machines and with hot material. The most common thickness, however, are 0.6 to 1.3 mm (0.024 to 0.050 in). Maximum thickness and size are limited only by the size of the equipment and the power available to make the metal flow.