Direct reduction processes can be divided roughly into two categories: gas-based and coal-based. In both cases, the objective of the process is to remove the oxygen contained in various forms of iron ore (sized ore, concentrates, pellets, mill scale, furnace dust, etc.) in order to convert the ore to metallic iron, without melting it (below 1,200 °C (2,190 °F)).
Plants for the production of pre-reduced iron ore are known as direct reduction plants. The principle involves exposing iron ore to the reducing action of a high-temperature gas (around 1000 °C). This gas is composed of carbon monoxide and dihydrogen, the proportions of which depend on the production process.
A bloomery is a type of metallurgical furnace once used widely for smelting iron from its oxides. The bloomery was the earliest form of smelter capable of smelting iron. Bloomeries produce a porous mass of iron and slag called a bloom. The mix of slag and iron in the bloom, termed sponge iron, is usually consolidated and further forged into ...
The sponge iron reaction (SIR) is a chemical process based on redox cycling of an iron-based contact mass, the first cycle is a conversion step between iron metal (Fe) and wuestite (FeO), the second cycle is a conversion step between wuestite (FeO) and magnetite (Fe 3 O 4). [1]
Cast iron development lagged in Europe because wrought iron was the desired product and the intermediate step of producing cast iron involved an expensive blast furnace and further refining of pig iron to cast iron, which then required a labor and capital intensive conversion to wrought iron.
The production of ferronickel from laterites takes place in a context that is much more favorable to the Krupp-Renn process than to the steel industry. Lateritic ores in the form of saprolite are poor, very basic and contain iron. Production volumes are moderate, and the nickel chemistry is remarkably amenable to rotary kiln reduction.
President-elect Donald Trump declared in a proposal out of left field on Tuesday that his administration will rename the Gulf of Mexico the "Gulf of America" in his latest attack on Mexico.
Austempering is defined by both the process and the resultant microstructure. Typical austempering process parameters applied to an unsuitable material will not result in the formation of bainite or ausferrite and thus the final product will not be called austempered.