Shotcrete, gunite (/ ˈ ɡ ʌ n aɪ t /), or sprayed concrete is concrete or mortar conveyed through a hose and pneumatically projected at high velocity onto a surface. This construction technique was invented by Carl Akeley and first used in 1907.
Shotcrete is also used for applications where seepage is an issue to limit the amount of water entering a construction site due to a high water table or other subterranean sources. This type of concrete is often used as a quick fix for weathering for loose soil types in construction zones. There are two application methods for shotcrete.
Many volumetric concrete mixer manufacturers have innovated the mixer in capacity and design, as well as added features including color, multiple admixes, fiber systems, and the ability to do gunite or shotcrete. The advantages of a volumetric mixer include: Reduces waste and associated costs by providing exact quantities.
Gunite may refer to: Shotcrete#Shotcrete vs. gunite, concrete or mortar conveyed through a hose; Gunite (horse), an American Thoroughbred race horse
The primary advantages of fibre-reinforced shotcrete are: Addition of steel fibers into the concrete improves the crack resistance (or ductility) capacity of the concrete. Traditional rebars are generally used to improve the tensile strength of the concrete in a particular direction, whereas steel fibers are useful for multidirectional ...
A period when for more than three successive days the average daily air temperature drops below 40 °F (~ 4.5 °C), and; Temperature stays below 50 °F (10 °C) for more than one-half of any 24-hour period. In Canada, where temperatures tend to be much lower during the cold season, the following criteria are used by CSA A23.1:
Shotcrete is a name that covers both dry and wet mix, so shotcrete is the better name for a topic containing both wet and dry mix sprayed concrete. Oyvind 10:26, August 30, 2005 (UTC) Reply- Gunite is the term for only the dry process and has been widely used in North America since the first development of the process around 1900.
This type of cement costs about the same as type I. Its typical compound composition is: 51% (C 3 S), 24% (C 2 S), 6% (C 3 A), 11% (C 4 AF), 2.9% MgO, 2.5% (SO 3), 0.8% ignition loss, and 1.0% free CaO. A limitation on the composition is that the (C 3 A) shall not exceed 8%, which reduces its vulnerability to sulphates. This type is for general ...