Young's modulus is defined as the ratio of the stress (force per unit area) applied to the object and the resulting axial strain (displacement or deformation) in the linear elastic region of the material. Although Young's modulus is named after the 19th-century British scientist Thomas Young, the concept was developed in 1727 by Leonhard Euler.
Elastic properties describe the reversible deformation (elastic response) of a material to an applied stress. They are a subset of the material properties that provide a quantitative description of the characteristics of a material, like its strength .
Young's modulus Density (g/cm 3) Young's modulus per density; specific stiffness (10 6 m 2 s −2) Young's modulus per density squared (10 3 m 5 kg −1 s −2) Young's modulus per density cubed (m 8 kg −2 s −2) Reference Latex foam, low density, 10% compression [4] 5.9 × 10 ^ −7: 0.06: 9.83 × 10 ^ −6: 0.000164: 0.00273: Reversible ...
The material of the beam is homogeneous 1 and isotropic 2. The value of Young's Modulus of Elasticity is same in tension and compression. The transverse sections which were plane before bending, remain plane after bending also. The beam is initially straight and all longitudinal filaments bend into circular arcs with a common centre of curvature.
The bulk modulus is an extension of Young's modulus to three dimensions. Flexural modulus ( E flex ) describes the object's tendency to flex when acted upon by a moment . Two other elastic moduli are Lamé's first parameter , λ, and P-wave modulus , M , as used in table of modulus comparisons given below references.
This fact follows from the symmetry of the stress and strain tensors, together with the requirement that the stress derives from an elastic energy potential. For isotropic materials, the elasticity tensor has just two independent components, which can be chosen to be the bulk modulus and shear modulus. [3]
The elastic modulus of a composite in the fiber direction of a unidirectional composite can be calculated using the following equation: = + Where: is the fiber volume ratio. and is the elastic modulus of the matrix
E 1 and E 2 are the Young's moduli in the 1- and 2-direction and G 12 is the in-plane shear modulus. v 12 is the major Poisson's ratio and v 21 is the minor Poisson's ratio. The flexibility matrix [S] is symmetric. The minor Poisson's ratio can hence be found if E 1, E 2 and v 12 are known.