Martensite has a lower density than austenite, so that the martensitic transformation results in a relative change of volume. [4] Of considerably greater importance than the volume change is the shear strain, which has a magnitude of about 0.26 and which determines the shape of the plates of martensite. [5]
Pearlite is a two-phased, lamellar (or layered) structure composed of alternating layers of ferrite (87.5 wt%) and cementite (12.5 wt%) that occurs in some steels and cast irons. During slow cooling of an iron-carbon alloy, pearlite forms by a eutectoid reaction as austenite cools below 723 °C (1,333 °F) (the eutectoid temperature).
The large density of dislocations in the ferrite present in bainite, and the fine size of the bainite platelets, makes this ferrite harder than it normally would be. [4] [5] The temperature range for transformation of austenite to bainite (125–550 °C) is between those for pearlite and martensite. In fact, there is no fundamental lower limit ...
The pearlite takes on longer, deeper scratches, and either appears shiny and bright, or sometimes dark depending on the viewing angle. The martensite is harder to scratch, so the microscopic abrasions are smaller. The martensite usually appears brighter yet flatter than the pearlite, and this is less dependent on the viewing angle. [12]
Normalizing not only produces pearlite but also martensite and sometimes bainite, which gives harder and stronger steel but with less ductility for the same composition than full annealing. In the normalizing process the steel is heated to about 40 degrees Celsius above its upper critical temperature limit, held at this temperature for some ...
Experts offer a list of the fish that have the most health benefits — from salmon and sardines to tilapia and tuna — plus which fish to avoid and why.
New Cold Foam Toppings. Along with returning favorite, a.k.a the peppermint chocolate cold foam, Starbucks is adding Gingerbread and Salted Pecan flavors to the roster.
As a result of the transformation, the microconstituents, pearlite and bainite, form; pearlite forms at higher temperatures and bainite at lower. TTT diagram of isothermal transformations of a hypoeutectoid carbon steel; showing the main components obtained when cooling the steel and its relation with the Fe-C phase diagram of carbon steels.