The progression of thicknesses is clear in column 3 (U.S. standard for sheet and plate iron and steel 64ths inch (delta)). The thicknesses vary first by 1 ⁄ 32 inch in higher thicknesses and then step down to increments of 1 ⁄ 64 inch, then 1 ⁄ 128 inch, with the final increments at decimal fractions of 1 ⁄ 64 inch.
So S355 has a minimum yield strength of 355 MPa for the smallest thickness range covered by the relevant standard – i.e. EN10025. [ 2 ] Below is a table indicating the most common application codes.
A36 steel has a Poisson's ratio of 0.26 and a shear modulus of 11,500 ksi (79.3 GPa). [7] A36 steel in plates, bars, and shapes with a thickness of less than 8 inches (203 millimeters) has a minimum yield strength of 36 ksi (250 MPa) and ultimate tensile strength of 58–80 ksi (400–550 MPa).
The material thicknesses for such thin-walled steel members usually range from 0.0147 in. (0.373 mm) to about ¼ in. (6.35 mm). Steel plates and bars as thick as 1 in. (25.4 mm) can also be cold-formed successfully into structural shapes (AISI, 2007b). [3]
On certified steels, the plates are marked with the grade and a preceding "AB/", e.g. AB/A etc. [3] Yield point for all ordinary-strength ABS steels is specified as 34,000 psi (235 MPa ), except for ABS A in thicknesses of greater than 1 inch (25 mm) which has yield strength of 32,000 psi (225 MPa), and cold flange rolled sections, which have ...
The tensile yield strength of A514 alloys is specified as at least 100 ksi (689 MPa) for thicknesses up to 2.5 inches (63.5 mm) thick plate, and at least 110 ksi (758 MPa) ultimate tensile strength, with a specified ultimate range of 110–130 ksi (758–896 MPa). Plates from 2.5 to 6.0 inches (63.5 to 152.4 mm) thick have specified strength of ...