Each mole of CO 2 (44 g) reacts with one mole of calcium hydroxide (74 g) and produces one mole of water (18 g). The reaction can be considered as a strong-base-catalysed, water-facilitated reaction. [5] The reaction mechanism of carbon dioxide with soda lime can be decomposed in three elementary steps:
Calcium hydroxide is moderately soluble in water, as seen for many dihydroxides. Its solubility increases from 0.66 g/L at 100 °C to 1.89 g/L at 0 °C. [8] Its solubility product K sp of 5.02 × 10 −6 at 25 °C, [1] its dissociation in water is large enough that its solutions are basic according to the following dissolution reaction:
Pure lime is soluble in water containing carbonic acid, a natural, weak acid which is a solution of carbon dioxide in water and acid rain so it will slowly wash away, but this characteristic also produces autogenous or self-healing process where the dissolved lime can flow into cracks in the material and be redeposited, automatically repairing ...
Carbonatation is a slow process that occurs in concrete where lime (CaO, or Ca(OH) 2 ) in the cement reacts with carbon dioxide (CO 2) from the air and forms calcium carbonate. The water in the pores of Portland cement concrete is normally alkaline with a pH in the range of 12.5 to 13.5.
This reaction can take place at anywhere above 840 °C (1,540 °F), but is generally considered to occur at 900 °C (1,650 °F) (at which temperature the partial pressure of CO 2 is 1 atmosphere), but a temperature around 1,000 °C (1,830 °F) (at which temperature the partial pressure of CO 2 is 3.8 atmospheres [1]) is usually used to make the ...
The temperature at which limestone yields calcium oxide is usually given as 825 °C, but stating an absolute threshold is misleading. Calcium carbonate exists in equilibrium with calcium oxide and carbon dioxide at any temperature. At each temperature there is a partial pressure of carbon
As it hydrates, an exothermic reaction results and the solid puffs up. The hydrate can be reconverted to quicklime by removing the water by heating it to redness to reverse the hydration reaction. One litre of water combines with approximately 3.1 kilograms (6.8 lb) of quicklime to give calcium hydroxide plus 3.54 MJ of energy.
As lime in the form of limewater is added to raw water, the pH is raised and the equilibrium of carbonate species in the water is shifted. Dissolved carbon dioxide (CO 2) is changed into bicarbonate (HCO − 3) and then carbonate (CO 2-3). This action causes calcium carbonate to precipitate due to exceeding the solubility product.