Superplasticizers (SPs), also known as high range water reducers, are additives used for making high-strength concrete or to place self-compacting concrete. Plasticizers are chemical compounds enabling the production of concrete with approximately 15% less water content. Superplasticizers allow reduction in water content by 30% or more.
Water reducers offer several advantages in their use, listed below: reduces the water content by 5-10%; decreases the concrete porosity; increases the concrete strength by up to 25% (as less water is required for the concrete mixture to remain workable) increases the workability (assuming the amount of free water remains constant)
In the concrete technology, plasticizers and superplasticizers are also called high range water reducers. When added to concrete mixtures, they confer a number of properties including improved workability and strength. The strength of concrete is inversely proportional to the amount of water added, i.e., the water-cement (w/c) ratio.
Self-consolidating concrete or self-compacting concrete (SCC) [1] is a concrete mix which has a low yield stress, high deformability, good segregation resistance (prevents separation of particles in the mix), and moderate viscosity (necessary to ensure uniform suspension of solid particles during transportation, placement (without external compaction), and thereafter until the concrete sets).
Ultrapure water (UPW), high-purity water or highly purified water (HPW) is water that has been purified to uncommonly stringent specifications. Ultrapure water is a term commonly used in manufacturing to emphasize the fact that the water is treated to the highest levels of purity for all contaminant types, including organic and inorganic compounds, dissolved and particulate matter, and ...
Global warming potential (GWP) of GGBS decreased by 1.1 kg CO 2 eq/m 3, while FA decreased by 17.3 kg CO 2 eq/m 3 when the mineral admixture replacement ratio was increased by 10%. This study also compared the compressive strength properties of binary blended low-carbon concrete according to the replacement ratios, and the applicable range of ...
A cement accelerator is an admixture for the use in concrete, mortar, rendering or screeds. The addition of an accelerator speeds the setting time and thus cure time starts earlier. [ 1 ] This allows concrete to be placed in winter with reduced risk of frost damage. [ 2 ]
More water is therefore used than is chemically and physically necessary to react with cement. Water–cement ratios in the range of 0.40 to 0.60 are typically used. For higher-strength concrete, lower w/c ratios are necessary, along with a plasticizer to increase flowability.