186 etched glass at Bankfield Museum. Glass etching, or " French embossing ", is a popular technique developed during the mid-1800s that is still widely used in both residential and commercial spaces today. Glass etching comprises the techniques of creating art on the surface of glass by applying acidic, caustic, or abrasive substances.
Polytetrafluoroethylene (PTFE), better known by its trade name Teflon, has many desirable properties which make it an attractive material for numerous industries. It has good chemical resistance, a low dielectric constant, low dielectric loss, and a low coefficient of friction, making it ideal for reactor linings, circuit boards, and kitchen utensils, to name a few applications.
Buffered oxide etch (BOE), also known as buffered HF or BHF, is a wet etchant used in microfabrication. It is a mixture of a buffering agent, such as ammonium fluoride NH4F, and hydrofluoric acid (HF). Its primary use is in etching thin films of silicon nitride (Si 3 N 4) or silicon dioxide (SiO 2), by the reaction: SiO2 + 4HF + 2NH4F → (NH4 ...
Sodium silicate is also the technical and common name for a mixture of such compounds, chiefly the metasilicate, also called waterglass, water glass, or liquid glass. The product has a wide variety of uses, including the formulation of cements , coatings, passive fire protection , textile and lumber processing, manufacture of refractory ...
Soda–lime glass (for containers) [2] Borosilicate (low expansion, similar to Pyrex, Duran) Glass wool (for thermal insulation) Special optical glass (similar to Lead crystal) Fused silica Germania glass Germanium selenide glass Chemical composition, wt% 74 SiO 2, 13 Na 2 O, 10.5 CaO, 1.3 Al 2 O 3, 0.3 K 2 O, 0.2 SO 3, 0.2 MgO, 0.01 TiO 2, 0. ...
Ammonium fluoride is a critical component of buffered oxide etch (BOE), a wet etchant used in microfabrication. It acts as the buffering agent in a solution of concentrated HF , creating an etchant with a more controllable rate of etching (than that of simple concentrated HF solutions).
A high-purity (≥99.9998%) aluminium bar that has been etched to reveal the component crystallites. Chemical milling or industrial etching is the subtractive manufacturing process of using baths of temperature-regulated etching chemicals to remove material to create an object with the desired shape. [1][2] Other names for chemical etching ...
The manufacturing process for soda–lime glass consists in melting the raw materials, which are the silica, soda, lime (in the form of (Ca(OH) 2), dolomite (CaMg(CO 3) 2, which provides the magnesium oxide), and aluminium oxide; along with small quantities of fining agents (e.g., sodium sulfate (Na 2 SO 4), sodium chloride (NaCl), etc.) in a glass furnace at temperatures locally up to 1675 ...