7068 alloy is a 7000 series aluminium-zinc alloy registered with the US Aluminium Association and produced to AMS 4331 (chemical composition and mechanical properties) and AMS 2772 (heat treatment). 7068 alloy ‘A’ and ‘B’ tensile data and fatigue properties have been ratified for inclusion in MIL Handbook 5 / MMPDS.
T6 temper 7075 has an ultimate tensile strength of 510–540 MPa (74,000–78,000 psi) and yield strength of at least 430–480 MPa (63,000–69,000 psi). It has a failure elongation of 5–11%. [9] The T6 temper is usually achieved by homogenizing the cast 7075 at 450 °C for several hours, quenching, and then ageing at 120 °C for 24 hours.
Aluminum: 97.3 Silicon: 1 Magnesium: 0.80 Manganese: 0.5 Copper: 0.35 Mechanical Properties. Properties [1] Metric Tensile strength 290 MPa Yield strength ...
Print/export Download as PDF; Printable version; In other projects Wikidata item; Appearance. ... Shear strength 62 MPa Elastic modulus 70-80 GPa
Typical material properties for 6060 aluminum alloy include: [2] Density: 2.710 g/cm 3, or 169 lb/ft 3. Young's modulus: 70 GPa, or 10 Msi, or 303 EMEC; Ultimate tensile strength: 140 to 230 MPa, or 20 to 33 ksi. Yield strength: 70 to 180 MPa, or 10 to 26 ksi. Thermal Expansion: 23.4 μm/m-K. Solidus: 610 °C or 1130 °F.
Unhardened 5086 has a yield strength of 120 MPa (17 ksi) and ultimate tensile strength of 260 MPa (38 ksi) from −28 to 100 °C (−18 to 212 °F). At cryogenic temperatures it is slightly stronger: at −196 °C (−321 °F), yield of 130 MPa (19 ksi) and ultimate tensile strength of 380 MPa (55 ksi); above 100 °C (212 °F) its strength is reduced.
Typical material properties for 6005A aluminum alloy include: [2] Density: 2.71 g/cm 3, or 169 lb/ft 3. Electrical Conductivity: 47 to 50% IACS. Young's modulus: 70 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Conductivity: 180 to 190 W/m-K.
The aluminium-copper alloys have high strength, but are generally less corrosion resistant and harder to weld than other types of aluminium alloys. To compensate for the lower corrosion resistance, 2219 aluminium can be clad in a commercially pure alloy such as 1050 or painted.