A Watts bath, named for its inventor Oliver Patterson Watts, is an aqueous electrolyte solution for plating nickel from a nickel anode. It can deposit both bright and semi-bright nickel. Bright nickel is typically used for decorative purposes and corrosion protection.
The main ingredients of an electroless nickel plating bath are source of nickel cations Ni 2+, usually nickel sulfate and a suitable reducing agent, such as hypophosphite H 2 PO − 2 or borohydride BH − 4. [1] With hypophosphite, the main reaction that produces the nickel plating yields orthophosphite H 2 PO − 3, elemental phosphorus ...
In the basic electroforming process, an electrolytic bath is used to deposit nickel or other electroformable metal onto a conductive surface of a model (mandrel). Once the deposited material has been built up to the desired thickness, the electroform is parted from the substrate.
The electrolyte in the electrolytic plating cell should contain positive ions (cations) of the metal to be deposited. These cations are reduced at the cathode to the metal in the zero valence state. For example, the electrolyte for copper electroplating can be a solution of copper(II) sulfate, which dissociates into Cu 2+ cations and SO 2− 4 ...
Initially based on ammonium chloride, options today include ammonium, potassium or mixed ammonium/potassium electrolytes. The chosen content of zinc depends on the required productivity and part configuration. High zinc improves the bath's efficiency (plating speed), while lower levels improve the bath's ability to throw into low current densities.
Electroless nickel-boron plating developed as a variant of the similar nickel-phosphorus process, discovered accidentally by Charles Adolphe Wurtz in 1844. [2]In 1969, Harold Edward Bellis from DuPont filed a patent for a general class of electroless plating processes using sodium borohydride, dimethylamine borane, or sodium hypophosphite, in the presence of thallium salts, thus producing a ...
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
cathode made of platinum or stainless steel (needle), anode nickel-plated or gold-plated copper or brass or polished steel, duration 10 s, distance between cathode and anode 3 mm . [20] An electrolyte of 100 g of litharge dissolved in 0.5 l of water can also be used in which 100 g of NaOH is dissolved.