In the recent past, HSS was commonly available in mild steel, such as A500 grade B. Today, HSS is commonly available in mild steel, A500 grade C. Other steel grades available for HSS are A847 (weathering steel), A1065 (large sections up to 50 inch sq made with SAW process), and recently approved A1085 (higher strength, tighter tolerances than ...
ASTM A500 is a standard specification published by the ASTM for cold-formed welded and seamless carbon steel structural tubing in round, square, and rectangular shapes. It is commonly specified in the US for hollow structural sections, but the more stringent CSA G40.21 is preferred in Canada. Another related standard is ASTM A501, which is a ...
Fig. 1: Critical stress vs slenderness ratio for steel, for E = 200 GPa, yield strength = 240 MPa. Euler's critical load or Euler's buckling load is the compressive load at which a slender column will suddenly bend or buckle. It is given by the formula: [1] = where
A36 steel has a Poisson's ratio of 0.26 and a shear modulus of 11,500 ksi (79.3 GPa). [7] A36 steel in plates, bars, and shapes with a thickness of less than 8 inches (203 millimeters) has a minimum yield strength of 36 ksi (250 MPa) and ultimate tensile strength of 58–80 ksi (400–550 MPa).
Steel never turns into a liquid below this temperature. Pure Iron ('Steel' with 0% Carbon) starts to melt at 1,492 °C (2,718 °F), and is completely liquid upon reaching 1,539 °C (2,802 °F). Steel with 2.1% Carbon by weight begins melting at 1,130 °C (2,070 °F), and is completely molten upon reaching 1,315 °C (2,399 °F).
There are four types of materials available: O-1 tool steel, A-2 tool steel, A-6 tool steel, and 1018 steel (low-carbon or low-carb steel). Lengths are either 18 or 36 in (457 or 914 mm) long, various widths up to 16 in (406 mm) are available, and thicknesses range from 1 ⁄ 64 to 2.875 in (0.40 to 73.03 mm).
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
Ultimate tensile strength of ordinary strength alloys is 58,000 - 71,000 psi (400-490 MPa), except for ABS A shapes and bars with 58,000 - 80,000 psi (400-550 MPa), and cold flanged sections with 55,000 - 65,000 psi (380-450 MPa). The various grades have slightly differing alloy chemical ingredients, and differing fracture toughness.