Tensile testing, also known as tension testing, [1] is a fundamental materials science and engineering test in which a sample is subjected to a controlled tension until failure. Properties that are directly measured via a tensile test are ultimate tensile strength , breaking strength , maximum elongation and reduction in area. [ 2 ]
Schematic and dimensions of a compact tension specimen. A compact tension specimen (CT) is a type of standard notched specimen in accordance with ASTM [1] and ISO [2] standards. Compact tension specimens are used extensively in the area of fracture mechanics and corrosion testing, in order to establish fracture toughness and fatigue crack ...
According to ASTM D1002 The specimens tested will be configured as lap joints. They will need to be sectioned in a way that they can fit in the grips used for the tensile testing. The length of the overlap for the lap joint is determined by the thickness of the material, the yield point of the metal, and the value that is 50% of the estimated ...
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
According to ASTM A370, [12] the standard specimen size for Charpy impact testing is 10 mm × 10 mm × 55 mm. Subsize specimen sizes are: 10 mm × 7.5 mm × 55 mm, 10 mm × 6.7 mm × 55 mm, 10 mm × 5 mm × 55 mm, 10 mm × 3.3 mm × 55 mm, 10 mm × 2.5 mm × 55 mm. Details of specimens as per ASTM A370 (Standard Test Method and Definitions for ...
The success of a biaxial tensile test is strictly related to the shape of the specimen. [17] The two most used geometries are the square and cruciform shapes. Dealing with fibrous materials or fibres reinforced composites , the fibres should be aligned to the load directions for both classes of specimens, in order to minimize the shear stresses ...
ASTM C1161: Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature; ASTM D6272: Standard Test Method for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials by Four-Point Bending; ASTM C393: Standard Test Method for Core Shear Properties of Sandwich Constructions by ...
The portion where necking occurs may be called the neck of the specimen. In engineering and materials science, necking is a mode of tensile deformation where relatively large amounts of strain localize disproportionately in a small region of the material. The resulting prominent decrease in local cross-sectional area provides the basis for the ...