Spray forming offers certain advantages over both conventional ingot metallurgy and more specialized techniques such as powder metallurgy.Firstly, it is a flexible process and can be used to manufacture a wide range of materials, some of which are difficult to produce by other methods, e.g. Al-5wt% Li alloys or Al-SiC, Al-Al 2 O 3 metal matrix composites (MMCs).
It is used for spraying pure metal powders with the sizes of 5–50 μm. In low-pressure cold spraying (LPCS), the working gas is a compressed gas with pressure 0.5–1.0 MPa, flow rate 0.5–2 m 3 /min and the heating power 3–5 kW. It is used for spraying a mechanical mixture of metal and ceramic powders.
Thermal spraying can provide thick coatings (approx. thickness range is 20 microns to several mm, depending on the process and feedstock), over a large area at high deposition rate as compared to other coating processes such as electroplating, physical and chemical vapor deposition. Coating materials available for thermal spraying include ...
Cold sprayable metal technology is a metallizing process that seamlessly applies cold sprayable or putty able metal to almost any surface. The composite metal consists of two (water-based binder) or three different ingredients: metal powder, binder and hardener. The mixture of the ingredients is cast or sprayed on the substrate at room temperature.
Cold spray additive manufacturing (CSAM) (also called cold spray 3D printing) is a particular application of cold spraying, able to fabricate freestanding parts or to build features on existing components. During the process, fine powder particles are accelerated in a high-velocity compressed gas stream, and upon the impact on a substrate or ...
Commonly the materials that are sprayed onto components during detonation spraying are powders of metals, metal alloys and cermets; as well as their oxides (aluminum, copper, iron, etc.). Detonation spraying is an industrial process that can be dangerous if not performed correctly and in a safe environment.
When a nozzle is used for cleaning, the impact or pressure is called impingement. As with all spray patterns, the unit impact decreases as the distance from the nozzle increases, thereby increasing the impact area size. The spray impact, , depends on the volumetric flowrate Q and pressure drop according to the equation below. The nozzle type ...
Solution precursor plasma spray (SPPS) is a thermal spray process where a feedstock solution is heated and then deposited onto a substrate. Basic properties of the process are fundamentally similar to other plasma spraying processes. However, instead of injecting a powder into the plasma plume, a liquid precursor is used.