A billet is a length of metal that has a round or square cross-section, with an area less than 36 in 2 (230 cm 2). Billets are created directly via continuous casting or extrusion or indirectly via hot rolling an ingot or bloom. [1] [2] [4] Billets are further processed via profile rolling and drawing. Final products include bar stock and wire. [3]
Bar stock, also (colloquially) known as blank, slug or billet, [1] is a common form of raw purified metal, used by industry to manufacture metal parts and products. Bar stock is available in a variety of extrusion shapes and lengths.
Continuous casting, also called strand casting, is the process whereby molten metal is solidified into a "semifinished" billet, bloom, or slab for subsequent rolling in the finishing mills.
Steel billets 130mm² ("pencil ingots") are heated to approximately 1200°C to 1250°C in a reheat furnace. Then, they are progressively rolled to reduce the billets to the final size and shape of reinforcing bar. After the last rolling stand, the billet moves through a quench box.
Mill scale on an anvil. Mill scale, often shortened to just scale, is the flaky surface of hot rolled steel, consisting of the mixed iron oxides iron(II) oxide (FeO, wüstite), iron(III) oxide (Fe 2 O 3, hematite), and iron(II,III) oxide (Fe 3 O 4, magnetite).
Thixocasting utilizes a pre-cast billet with a non-dendritic microstructure that is normally produced by vigorously stirring the melt as the bar is being cast. Induction heating is normally used to re-heat the billets to the semi-solid temperature range, and die casting machines are used to inject the semi-solid material into hardened steel ...
The term long products may include hot rolled bar, cold rolled or drawn bar, rebar, railway rails, wire, rope (stranded wire), woven cloth of steel wire, shapes (sections) such as U, I, or H sections, and may also include ingots from continuous casting, including blooms and billets. Fabricated structural units, such bridge sections are also ...
Billets are hot or cold rolled into bars, rods, and wire. Blooms are hot or cold rolled into structural steel, such as I-beams and rails. In modern steel mills these processes often occur in one assembly line, with ore coming in and finished steel products coming out. [17]