Example of flat piece of concrete having dislodged with corroded rebar underneath, Welland River bridge across Queen Elizabeth Way in Niagara Falls, Ontario. The expansion of the corrosion products (iron oxides) of carbon steel reinforcement structures may induce internal mechanical stress (tensile stress) that cause the formation of cracks and disrupt the concrete structure.
Fretting refers to wear and sometimes corrosion damage of loaded surfaces in contact while they encounter small oscillatory movements tangential to the surface. Fretting is caused by adhesion of contact surface asperities, which are subsequently broken again by the small movement. This breaking causes wear debris to be formed.
The individual gaps are sealed by watertight elastomeric profiles, and surface beam movements are regulated by an elastic control system. The drainage of the joint is via the drainage system of the bridge deck. Certain joints feature so-called “sinus plates” on their surface, which reduce noise from over-passing traffic by up to 80%. [2]
The initiation time is related to the rate at which carbonation propagates in the concrete cover thickness.Once that carbonation reaches the steel surface, altering the local pH value of the environment, the protective thin film of oxides on the steel surface becomes instable, and corrosion initiates involving an extended portion of the steel surface.
To attempt to simplify and to stylize a very complex set of various reactions, the whole ASR reaction, after its complete evolution (ageing process) in the presence of sufficient Ca 2+ cations available in solution, could be compared to the pozzolanic reaction which would be catalysed by the undesirable presence of excessive concentrations of alkali hydroxides (NaOH and KOH) in the concrete.
Cathodic protection (CP; / k æ ˈ θ ɒ d ɪ k / ⓘ) is a technique used to control the corrosion of a metal surface by making it the cathode of an electrochemical cell. [1] A simple method of protection connects the metal to be protected to a more easily corroded " sacrificial metal " to act as the anode .
These values have to be used cautiously as there is strong evidence that chloride diffusion and surface electrical resistivity is dependent on other factors such as mix composition and age. [6] The electrical resistivity of the concrete cover layer decreases due to: [7] Increasing concrete water content; Increasing concrete porosity; Increasing ...
A precast concrete walled house under construction An example of low-quality precast concrete with exposed dowels, connectors, indications of cracks, and malformations, even during its installation, Barangay Lantic, Carmona, Cavite, Philippines Interior view of the walls, supports, and roof of a precast commercial shop in Williston, North Dakota, US.