The glass transition of a liquid to a solid-like state may occur with either cooling or compression. [10] The transition comprises a smooth increase in the viscosity of a material by as much as 17 orders of magnitude within a temperature range of 500 K without any pronounced change in material structure. [11]
Vitrification (from Latin vitrum ' glass ', via French vitrifier) is the full or partial transformation of a substance into a glass, [1] that is to say, a non-crystalline or amorphous solid. Glasses differ from liquids structurally and glasses possess a higher degree of connectivity with the same Hausdorff dimensionality of bonds as crystals ...
Vitrified sand is sand that has been heated to a high enough temperature to undergo vitrification, which is the melting of the silicon dioxide or quartz that compose common sand. Vitrified sand is a type of natural glass, contrasted with manufactured glass in which soda ash or potash are added to lower the melting point. Pure quartz melts at ...
Sodium silicate glass-to-glass bonding has the advantage that it is a low-temperature bonding technique, as opposed to fusion bonding. [21] It also requires less processing than glass-to-glass anodic bonding, [23] which requires an intermediate layer such as silicon nitride (SiN) to act as a diffusion barrier for sodium ions. [23]
An estimated 4,300 gigajoules (4.3 × 10 19 erg) of heat energy went into forming the glass. As the temperature required to melt the sand into the observed glass form was about 1,470 °C (2,680 °F), this was estimated to have been the minimum temperature the sand was exposed to. [16]
The change from supercooled liquid to glass occurs at a temperature called the glass transition temperature, which depends on both cooling rate and the amount of water dissolved in the magma. Magma rich in silica and poor in dissolved water is most easily cooled rapidly enough to form volcanic glass.
Deformation point (Glass deforms under its own weight on the μm-scale within a few hours.) 11–12.3 12–13.3 Glass transition temperature, T g: 12 13 Annealing point (Stress is relieved within several minutes.) 13.5 14.5 Strain point (Stress is relieved within several hours.)
Fragility characterizes how rapidly the viscosity of a glass forming liquid approaches a very large value approximately 10 12 Pa s during cooling. At this viscosity, the liquid is "frozen" into a solid and the corresponding temperature is known as the glass transition temperature T g. Materials with a higher fragility have a more rapid increase ...