Galvanization (also spelled galvanisation) [1] is the process of applying a protective zinc coating to steel or iron, to prevent rusting. The most common method is hot-dip galvanizing, in which the parts are coated by submerging them in a bath of hot, molten zinc. [citation needed]
In 1742, French chemist Paul Jacques Malouin described a method of coating iron by dipping it in molten zinc in a presentation to the French Royal Academy.. In 1772, Luigi Galvani, for whom galvanizing was named, discovered the electrochemical process that takes place between metals during an experiment with frog legs.
In order to develop the excellent properties of zinc flake coatings, an annealing process is required. The coated parts have to be cured inside an oven at a controlled temperature for a set period. This temperature/time configuration is dependent on the coating material and the product manufacturer, as each manufacturer of zinc flake products ...
Immersion zinc plating is an electroless (non-electrolytic) coating process that deposits a thin layer of zinc on a less electronegative metal, by immersion in a solution containing a zinc or zincate ions, Zn(OH) 2− 4. A typical use is plating aluminum with zinc prior to electrolytic or electroless nickel plating.
Electrogalvanizing is a process in which a layer of zinc is bonded to steel to protect against corrosion, enhance adhesion, or give an aesthetic appeal.The process involves electroplating, running a current of electricity through a saline-/zinc-based electrolytic solution with a zinc anode and steel cathode.
With these process improvements, the end result was that a low-temperature (energy-efficient) zinc phosphating (Parkerizing) process, using strategic materials to which the United States had ready access, became the most common phosphating process used during World War II to protect American war materials such as firearms and planes from rust ...
Sherardising is a process of galvanization of ferrous metal surfaces, also called vapour galvanising and dry galvanizing.The process is named after British metallurgist Sherard Osborn Cowper-Coles (son of naval inventor Cowper Phipps Coles) who invented and patented the method c. 1900.
The coil coating process may be used for other substrates such as aluminium, or aluminium, stainless steel or alloy coated steel other than "pure" zinc coated steel. However, only "pure" zinc coated steel is typically referred to as PPGI. For example, PPGL may be used for pre-painted 55%Al/Zn alloy-coated steel (pre-painted GALVALUME(r) steel*)