Simulation of the outside of the Space Shuttle as it heats up to over 1,500 °C (2,730 °F) during re-entry into the Earth's atmosphere Bearing components made from 100% silicon nitride Si 3 N 4 Ceramic bread knife. Ceramic engineering is the science and technology of creating objects from inorganic, non-metallic materials. This is done either ...
Ceramic material is an inorganic, metallic oxide, nitride, or carbide material. Some elements, such as carbon or silicon, may be considered ceramics. Ceramic materials are brittle, hard, strong in compression, and weak in shearing and tension. They withstand the chemical erosion that occurs in other materials subjected to acidic or caustic ...
In both types of extrusion the raw material must be plasticized to allow and induce the flow of the material in the process. Complex technical ceramic parts are commonly formed using either the injection moulding process or "hot wax moulding." Both rely on heat sensitive plasticizers to allow material flow into a die.
Chemical vapour infiltration (CVI) is a ceramic engineering process whereby matrix material is infiltrated into fibrous preforms by the use of reactive gases at elevated temperature to form fiber-reinforced composites. [1] The earliest use of CVI was the infiltration of fibrous alumina with chromium carbide. [2]
Compaction of ceramic powders is a forming technique for ceramics in which granular ceramic materials are made cohesive through mechanical densification, either by hot or cold pressing. The resulting green part must later be sintered in a kiln. The compaction process permits an efficient production of parts to close tolerances with low drying ...
The crystal growth process is of considerable importance in determining the morphology of the produced glass ceramic composite material. Crystal growth is primarily dependent on two factors. First, it is dependent upon the rate at which the disordered structure can be re-arranged into a periodic lattice with longer-range order.
Glazing in pottery is the process of applying a coating or layer of material to ceramics that, when fired, forms a vitreous or glass-like surface. Glazes enhance the aesthetic appeal of pottery, provide a waterproof barrier, and improve its durability. Below are the major types of glazing commonly used in pottery: 1.
Hot isostatic pressing (HIP) is a manufacturing process, used to reduce the porosity of metals and increase the density of many ceramic materials. This improves the material's mechanical properties and workability. The process can be used to produce waste form classes.