The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
ASTM A500 is a standard specification published by the ASTM for cold-formed welded and seamless carbon steel structural tubing in round, square, and rectangular shapes. It is commonly specified in the US for hollow structural sections, but the more stringent CSA G40.21 is preferred in Canada.
The yield strength or yield stress is a material property and is the stress corresponding to the yield point at which the material begins to deform plastically. The yield strength is often used to determine the maximum allowable load in a mechanical component, since it represents the upper limit to forces that can be applied without producing ...
Volume, modulus of elasticity, distribution of forces, and yield strength affect the impact strength of a material. In order for a material or object to have a high impact strength, the stresses must be distributed evenly throughout the object. It also must have a large volume with a low modulus of elasticity and a high material yield strength. [7]
ASTM A992 steel has the following minimum mechanical properties, according to ASTM specification A992/A992M. Tensile yield strength, 345 MPa (50 ksi); tensile ultimate strength, 450 MPa (65 ksi); strain to rupture (sometimes called elongation ) in a 200-mm-long test specimen, 18%; strain to rupture in a 50-mm-long test specimen, 21%.
As shown later in this article, at the onset of yielding, the magnitude of the shear yield stress in pure shear is √3 times lower than the tensile yield stress in the case of simple tension. Thus, we have: = where is tensile yield strength of the material. If we set the von Mises stress equal to the yield strength and combine the above ...
A36 steel has a Poisson's ratio of 0.26 and a shear modulus of 11,500 ksi (79.3 GPa). [ 7 ] A36 steel in plates, bars, and shapes with a thickness of less than 8 inches (203 millimeters) has a minimum yield strength of 36 ksi (250 MPa ) and ultimate tensile strength of 58–80 ksi (400–550 MPa).
The tensile yield strength of A514 alloys is specified as at least 100 ksi (689 MPa) for thicknesses up to 2.5 inches (63.5 mm) thick plate, and at least 110 ksi (758 MPa) ultimate tensile strength, with a specified ultimate range of 110–130 ksi (758–896 MPa). Plates from 2.5 to 6.0 inches (63.5 to 152.4 mm) thick have specified strength of ...