The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
Mild steel has a relatively low tensile strength, but it is cheap and easy to form. Surface hardness can be increased with carburization. [3] The density of mild steel is approximately 7.85 g/cm 3 (7,850 kg/m 3; 0.284 lb/cu in) [4] and the Young's modulus is 200 GPa (29 × 10 ^ 6 psi). [5]
Minimum Yield Strength: B: Steel for reinforced concrete: Characteristic Yield Case: R: Steel for rail use: Minimum Yield Case: H: High Tensile Strength Flat products: Minimum Yield Case: If followed by T then the given mechanical property is minimum tensile strength D: Flat Products for Cold Forming: Followed by C, D or X and two numbers ...
A36 steel has a Poisson's ratio of 0.26 and a shear modulus of 11,500 ksi (79.3 GPa). [7] A36 steel in plates, bars, and shapes with a thickness of less than 8 inches (203 millimeters) has a minimum yield strength of 36 ksi (250 MPa) and ultimate tensile strength of 58–80 ksi (400–550 MPa).
In this case 0.6 applies to the example steel, known as EN8 bright, although it can vary from 0.58 to 0.62 depending on application. EN8 bright has a tensile strength of 800 MPa and mild steel, for comparison, has a tensile strength of 400 MPa. To calculate the force to shear a 25 mm diameter bar of EN8 bright steel;
The 32 grades have yield strength of 45,500 psi (315 MPa), and ultimate tensile strength of 64,000 - 85,000 psi (440-590 MPa). The 36 grades have yield strength of 51,000 psi (355 MPa), and ultimate tensile strength of 71,000 - 90,000 psi (490-620 MPa). Per Steel Vessel Rules Part 2 Chapter 1 Section 3 Table 2 (pg 36).
ASTM A500 defines four grades of carbon steel based primarily on material strength. [ 1 ] This is a standard set by the standards organization ASTM International , a voluntary standards development organization that sets technical standards for materials, products, systems, and services.
The ultimate strength is the maximum stress that a material can withstand before it breaks or weakens. [12] For example, the ultimate tensile strength (UTS) of AISI 1018 Steel is 440 MPa. In Imperial units, the unit of stress is given as lbf/in 2 or pounds-force per square inch. This unit is often abbreviated as psi.