Therefore, when concreting at cold temperature cannot be avoided, it is essential to have a minimum curing time at a temperature sufficiently above the freezing point of the concrete pore water, so that the early strength of concrete is high enough to resist the inner tensile stress caused by water freezing. [5]
3 Code of Practices for plain and reinforced concrete etc. IS 456 – 2000 4 Methods of sampling and analysis of concrete IS 1199 – 1959 5 Recommended Guide Lines for Concrete Mix Design IS 10262 – 1982 (F) Curing Compound; 1 Standard test method for water retention & daylight reflection test on concrete. ASTM-C-156809
The addition of an accelerator speeds the setting time and thus curing starts earlier. [1] This allows concrete to be placed in winter with reduced risk of frost damage. [2] Concrete is damaged if it does not reach a strength of 500 pounds per square inch (3.4 MPa) before freezing. [3] Typical cement accelerators are calcium nitrate (Ca(NO 3)
Accelerated curing is any method by which high early age strength is achieved in concrete. These techniques are especially useful in the prefabrication industry, wherein high early age strength enables the removal of the formwork within 24 hours, thereby reducing the cycle time, resulting in cost-saving benefits. [ 1 ]
"Freeze-Thaw resistance". Polymers in Concrete. CRC Press. pp. 40–42. ISBN 9780849348150. J. Marchand; Michel Pigeon; M. Setzer (1997). Freeze–thaw Durability of Concrete. Proceedings of the International Workshop in the Resistance of Concrete to Scaling Due to Freezing in the Presence of De-icing Salts, Sainte-Foy, Québec, Canada.
The ultimate strength of concrete is influenced by the water-cementitious ratio (w/cm), the design constituents, and the mixing, placement and curing methods employed.All things being equal, concrete with a lower water-cement (cementitious) ratio makes a stronger concrete than that with a higher ratio. [2]
Air entrainment in concrete is the intentional creation of tiny air bubbles in a batch by adding an air entraining agent during mixing. A form of surfactant (a surface-active substance that in the instance reduces the surface tension between water and solids) it allows bubbles of a desired size to form.
To limit self-desiccation shrinkage during hardening, SAPs were added as an internal curing agent in cementitious systems with a low water-to-binder ratio. Aside from reducing autogenous shrinkage, SAPs may be added to cementitious materials to improve freeze-thaw resistance and induce self-sealing and self-healing properties. In terms of the ...