Spray forming offers certain advantages over both conventional ingot metallurgy and more specialized techniques such as powder metallurgy.Firstly, it is a flexible process and can be used to manufacture a wide range of materials, some of which are difficult to produce by other methods, e.g. Al-5wt% Li alloys or Al-SiC, Al-Al 2 O 3 metal matrix composites (MMCs).
Thermal spraying can provide thick coatings (approx. thickness range is 20 microns to several mm, depending on the process and feedstock), over a large area at high deposition rate as compared to other coating processes such as electroplating, physical and chemical vapor deposition. Coating materials available for thermal spraying include ...
Electrostatic spray-assisted vapour deposition (ESAVD) is a technique (developed by a company called IMPT) to deposit both thin and thick layers of a coating onto various substrates. In simple terms chemical precursors are sprayed across an electrostatic field towards a heated substrate, the chemicals undergo a controlled chemical reaction and ...
It is used for spraying pure metal powders with the sizes of 5–50 μm. In low-pressure cold spraying (LPCS), the working gas is a compressed gas with pressure 0.5–1.0 MPa, flow rate 0.5–2 m 3 /min and the heating power 3–5 kW. It is used for spraying a mechanical mixture of metal and ceramic powders.
Cold spray additive manufacturing (CSAM) (also called cold spray 3D printing) is a particular application of cold spraying, able to fabricate freestanding parts or to build features on existing components. During the process, fine powder particles are accelerated in a high-velocity compressed gas stream, and upon the impact on a substrate or ...
Evaporation takes place in a vacuum, i.e. vapors other than the source material are almost entirely removed before the process begins. In high vacuum (with a long mean free path), evaporated particles can travel directly to the deposition target without colliding with the background gas. (By contrast, in the boiling pot example, the water vapor ...
In the metal organic chemical vapor deposition (MOCVD) technique, reactant gases are combined at elevated temperatures in the reactor to cause a chemical interaction, resulting in the deposition of materials on the substrate. A reactor is a chamber made of a material that does not react with the chemicals being used.
Cold sprayable metal technology is a metallizing process that seamlessly applies cold sprayable or putty able metal to almost any surface. The composite metal consists of two (water-based binder) or three different ingredients: metal powder, binder and hardener. The mixture of the ingredients is cast or sprayed on the substrate at room temperature.