ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy Extruded Bars, Rods, Wire, Profiles, and Tubes; ASTM B308/308M: Standard Specification for Aluminum-Alloy 6061-T6 Standard Structural Profiles; ASTM B483: Standard Specification for Aluminum and Aluminum-Alloy Drawn Tube and Pipe for General Purpose Applications
Typical material properties for 6005A aluminum alloy include: [2] Density: 2.71 g/cm 3, or 169 lb/ft 3. Electrical Conductivity: 47 to 50% IACS. Young's modulus: 70 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Conductivity: 180 to 190 W/m-K.
Typical material properties for 6005 aluminium alloy include: [2] Density: 2.70 g/cm 3, or 169 lb/ft 3. Young's modulus: 69 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Expansion: 23 μm/m-K.
Some items of sports equipment, which rely on high performance materials, have been made with scandium–aluminium alloys, including baseball bats, [56] lacrosse sticks, as well as bicycle [57] frames and components, and tent poles. U.S. gunmaker Smith & Wesson produces revolvers with frames composed of scandium alloy and cylinders of titanium ...
3004 aluminium alloy is an alloy in the wrought aluminium-manganese alloys family (3000 or 3xxx series). It is similar to the 3003 alloy, except for the addition of approximately 1% magnesium.
6060 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is much more closely related to the alloy 6063 than to 6061.The main difference between 6060 and 6063 is that 6063 has a slightly higher magnesium content.
T1 temper 6063 has an ultimate tensile strength of at least 120 MPa (17,000 psi) in thicknesses up to 12.7 mm (0.5 in), and 110 MPa (16,000 psi) from 13 to 25 mm (0.5 to 1 in) thick, and yield strength of at least 62 MPa (9,000 psi) in thickness up to 13 millimetres (0.5 in) and 55 MPa (8,000 psi) from 13 mm (0.5 in) thick.
Autoclaved aerated concrete (AAC) is a lightweight, precast, cellular concrete building material. It is eco-friendly, and suitable for producing concrete-like blocks . [ 1 ] It is composed of quartz sand , calcined gypsum , lime , portland cement , water, and aluminium powder .