Tensile testing, also known as tension testing, [1] is a fundamental materials science and engineering test in which a sample is subjected to a controlled tension until failure. Properties that are directly measured via a tensile test are ultimate tensile strength , breaking strength , maximum elongation and reduction in area. [ 2 ]
Schematic and dimensions of a compact tension specimen. A compact tension specimen (CT) is a type of standard notched specimen in accordance with ASTM [1] and ISO [2] standards. Compact tension specimens are used extensively in the area of fracture mechanics and corrosion testing, in order to establish fracture toughness and fatigue crack ...
A biaxial tensile test generally ... forces explicated by the specimen. The dimensions of the sample have to ... ASTM D5617 – 04(2015) – Standard Test Method for ...
ASTM A992 steel has the following minimum mechanical properties, according to ASTM specification A992/A992M. Tensile yield strength, 345 MPa (50 ksi); tensile ultimate strength, 450 MPa (65 ksi); strain to rupture (sometimes called elongation ) in a 200-mm-long test specimen, 18%; strain to rupture in a 50-mm-long test specimen, 21%.
According to ASTM A370, [12] the standard specimen size for Charpy impact testing is 10 mm × 10 mm × 55 mm. Subsize specimen sizes are: 10 mm × 7.5 mm × 55 mm, 10 mm × 6.7 mm × 55 mm, 10 mm × 5 mm × 55 mm, 10 mm × 3.3 mm × 55 mm, 10 mm × 2.5 mm × 55 mm. Details of specimens as per ASTM A370 (Standard Test Method and Definitions for ...
This test is performed on a universal testing machine (tensile testing machine or tensile tester) with a three-point or four-point bend fixture. The main advantage of a three-point flexural test is the ease of the specimen preparation and testing.
One example is the long used Sustained Load Test of notched round bar tensile specimens found in ASTM F 519. In this test, the exposed test specimens are subjected to a load equal to 75% of the Fracture Strength and held for 200 hours. If the specimen does not break, the specimen has passed. If it fractures prior to the 200 hours then it has ...
The ASTM standard E1820 for the measurement of fracture toughness [11] recommends three coupon types for fracture toughness testing, the single-edge bending coupon [SE(B)], the compact tension coupon [C(T)] and the disk-shaped compact tension coupon [DC(T)]. Each specimen configuration is characterized by three dimensions, namely the crack ...