The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
ASTM A992 steel has the following minimum mechanical properties, according to ASTM specification A992/A992M. Tensile yield strength, 345 MPa (50 ksi); tensile ultimate strength, 450 MPa (65 ksi); strain to rupture (sometimes called elongation ) in a 200-mm-long test specimen, 18%; strain to rupture in a 50-mm-long test specimen, 21%.
The ultimate strength is the maximum stress that a material can withstand before it breaks or weakens. [12] For example, the ultimate tensile strength (UTS) of AISI 1018 Steel is 440 MPa. In Imperial units, the unit of stress is given as lbf/in 2 or pounds-force per square inch. This unit is often abbreviated as psi.
Steel for rail use: Minimum Yield Case: H: High Tensile Strength Flat products: Minimum Yield Case: If followed by T then the given mechanical property is minimum tensile strength D: Flat Products for Cold Forming: Followed by C, D or X and two numbers characterising steel T: Tinmill Products: Nominal Yield Case: M: Electrical Steel: Number ...
Download as PDF; Printable version; ... 4340 steel is an ultra-high strength steel classified a medium-carbon, ... tensile strengths of 860-1980 MPa, elongations of ...
It has a yield strength up to 80,000 psi (550 MPa) but costs only 24% more than A36 steel (36,000 psi (250 MPa)). One of the disadvantages of this steel is that it is 30 to 40% less ductile . In the U.S., these steels are dictated by the ASTM standards A1008/A1008M and A1011/A1011M for sheet metal and A656/A656M for plates.
A572 Steel Material Properties, Per ASTM Standards [2]; A572 Grade Yield Point (KSI) [MPa] Tensile Strength (KSI) [MPa] Min. 8” Elongation % Grade 42
The tensile yield strength of A514 alloys is specified as at least 100 ksi (689 MPa) for thicknesses up to 2.5 inches (63.5 mm) thick plate, and at least 110 ksi (758 MPa) ultimate tensile strength, with a specified ultimate range of 110–130 ksi (758–896 MPa). Plates from 2.5 to 6.0 inches (63.5 to 152.4 mm) thick have specified strength of ...