Refractory materials are classified into three types based on fusion temperature (melting point). Normal refractories have a fusion temperature of 1580–1780 °C (e.g. fire clay) High refractories have a fusion temperature of 1780–2000 °C (e.g. chromite) Super refractories have a fusion temperature of > 2000 °C (e.g. zirconia)
In Middle and South Europe, grog is used to create fire-resistant chamotte type bricks and mortar for construction of fireplaces, old-style and industrial furnaces, and as component of high temperature application sealants and adhesives. A typical example of domestic use is a pizza stone made from chamotte. Because the stone can absorb heat ...
SiAlON ceramics are a specialist class of high-temperature refractory materials, with high strength at ambient and high temperatures, good thermal shock resistance and exceptional resistance to wetting or corrosion by molten non-ferrous metals, compared to other refractory materials such as, for example, alumina. A typical use is with handling ...
The strength and high-temperature stability of refractory metals make them suitable for hot metalworking applications and for vacuum furnace technology. Many special applications exploit these properties: for example, tungsten lamp filaments operate at temperatures up to 3073 K, and molybdenum furnace windings withstand 2273 K.
The purpose of the refractory lining is to insulate the steel shell from the high temperatures inside the kiln, and to protect it from the corrosive properties of the process material. It may consist of refractory bricks or cast refractory concrete, or may be absent in zones of the kiln that are below approximately 250 °C (482 °F).
After building of a new refractory-lined industrial furnace or equipment, or refractory maintenance or relining of existing equipment, a necessary step is the start-up of the operation, which usually involves heating-up the unit in a controllable way, in order to prevent spalling or shortening of the materials' predicted lifetime.
Ultra-high-temperature ceramics (UHTCs) are a type of refractory ceramics that can withstand extremely high temperatures without degrading, often above 2,000 °C. [1] They also often have high thermal conductivities and are highly resistant to thermal shock, meaning they can withstand sudden and extreme changes in temperature without cracking or breaking.
On the other side bulk ceramics made of ultra-high temperature ceramics (e.g. ZrB 2, HfB 2, or their composites) are hard materials which show low erosion even above 2000 °C but are heavy and suffer of catastrophic fracture and low thermal shock resistance compared to CMCs. Failure is easily under mechanical or thermo-mechanical loads because ...