Iron powder is commonly used for sintering. Powder metallurgy (PM) is a term covering a wide range of ways in which materials or components are made from metal powders.PM processes are sometimes used to reduce or eliminate the need for subtractive processes in manufacturing, lowering material losses and reducing the cost of the final product. [1]
The starting point for the tape casting process is the powder that the 'tape' is to be consisting of. This is the active component of the final product and the other contents, such as binder material and solvents have to be compatible with the powder. The powder is in general very fine, with maximum particle sizes of 5 micrometers. [8]
The study of sintering in metallurgical powder-related processes is known as powder metallurgy. An example of sintering can be observed when ice cubes in a glass of water adhere to each other, which is driven by the temperature difference between the water and the ice.
The function principles of the mechanic press machines differ in how to ensure the upper punch–main movement by cams, spindles-and friction drives, eccentric, knuckle-joints or by the round table principle, independent if the die-or lower punch movement is realized by cams- or eccentric systems or other mechanically or hydraulically combined systems.
Hot pressing is a high-pressure, low-strain-rate powder metallurgy process for forming of a powder or powder compact at a temperature high enough to induce sintering and creep processes. [1] This is achieved by the simultaneous application of heat and pressure. Hot pressing is mainly used to fabricate hard and brittle materials.
The following processes can be used to produce metal powder: [6] Direct reduction is the result of blending carbon with iron oxide ore, heating the mixture, removing the sponge iron from the carbon, grinding it, annealing it, and regrinding to make the powder form usable for manufacturing.
AOL
In the direct powder rolling (DPR) process BE powder is used to produce sheet and plate and composite multilayered sheet and plates. Sheets between 1.27 and 2.54 mm and 50 to 99+% dense of single layer CP titanium, Ti Grade 5, TiAl (Ti-48Al-2Cr-2Nb) and composite Ti/Grade 5/Ti and Grade 5/TiAl/Grade 5 have been produced by DPR and sintering.