Degraded concrete and rusted, exposed reinforcement bar (rebar) on Welland River bridge of the Queen Elizabeth Way in Niagara Falls, Ontario. Concrete degradation may have many different causes. Concrete is mostly damaged by the corrosion of reinforcement bars due to the carbonatation of hardened cement paste or
ASTM C1293: "Test Method for Concrete Aggregates by Determination of Length Change of Concrete Due to Alkali-Silica Reaction". It is a long-term confirmation test (1 or 2 years) at 38 °C in a water-saturated moist atmosphere (inside a thermostated oven) with concrete prisms containing the aggregates to be characterised mixed with a high-alkali ...
Concrete has a total embodied energy of 1.69 GJ/tonne, lower per unit mass than most common building materials besides wood. However, concrete structures often have high masses, so this comparison is not always directly relevant to decision making. Additionally, this value is based only on mix proportions of up to 20% fly ash.
According to the Michigan Concrete Association, ice melters can cause damage to concrete—particularly new concrete. When it snows and the ice starts to melt, the water that soaks in the concrete ...
Concrete from a joint in Boston’s Prudential Tunnel collapsed on Friday, causing damage to vehicles. Despite the event there were no reported injuries according to Massachusetts transportation ...
The conversion of calcium hydroxide in the concrete into calcium carbonate from absorption of CO 2 over several decades further strengthens the concrete and makes it more resistant to damage. This carbonation reaction, however, lowers the pH of the cement pore solution and can corrode the reinforcement bars.
Concrete sealers are applied to concrete to protect it from surface damage, corrosion, and staining. They either block the pores in the concrete to reduce absorption of water and salts or form an impermeable layer which prevents such materials from passing.
A fairly well-defined reaction front can often be observed in thin sections; ahead of the front the concrete is normal, or near normal. Behind the reaction front, the composition and the microstructure of concrete are modified. These changes may vary in type or severity but commonly include: Extensive cracking; Expansion