Vickers hardness numbers are reported as xxxHVyy, e.g. 440HV30, or xxxHVyy/zz if duration of force differs from 10 s to 15 s, e.g. 440HV30/20, where: 440 is the hardness number, HV names the hardness scale (Vickers), 30 indicates the load used in kgf. 20 indicates the loading time if it differs from 10 s to 15 s
Vickers hardness test; Brinell scale This page was last edited on 16 November 2024, at 12:16 (UTC). Text is available under the Creative Commons ...
A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels .
Some solid substances that are not minerals have been assigned a hardness on the Mohs scale. Hardness may be difficult to determine, or may be misleading or meaningless, if a material is a mixture of two or more substances; for example, some sources have assigned a Mohs hardness of 6 or 7 to granite but it is a rock made of several minerals ...
Whereas the Vickers scale is widely accepted as a most common test, [11] there remain controversies on the weight load to be applied during the test. This is because Vickers hardness values are load-dependent. An indent made with 0.5N will indicate a higher hardness value than an indent made with 50N.
A Vickers hardness tester. There are three main types of hardness measurements: scratch, indentation, and rebound. Within each of these classes of measurement there are individual measurement scales. For practical reasons conversion tables are used to convert between one scale and another.
There are several scales of durometer, used for materials with different properties. The two most common scales, using slightly different measurement systems, are the ASTM D2240 type A and type D scales. The A scale is for softer ones, while the D scale is for harder ones. The image of Bareiss digital durometer is shown in the photo.
The Vickers test has a great advantage of using one hardness scale to test all materials. The first reference to the Vickers indenter with low loads was made in the annual report of the National Physical Laboratory in 1932. Lips and Sack describes the first Vickers tester using low loads in 1936. [citation needed]