A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels .
Mohs hardness [1] Vickers hardness (MPa) [1] Brinell hardness (MPa) [1] Brinell hardness (MPa) [note 1] [2] 3: Li: lithium: 0.6: 5: 4: Be: beryllium: 5.5: 1670: 590 ...
The Vickers hardness test was developed in 1921 by Robert L. Smith and George E. Sandland at Vickers Ltd as an alternative to the Brinell method to measure the hardness of materials. [1] The Vickers test is often easier to use than other hardness tests since the required calculations are independent of the size of the indenter, and the indenter ...
The Brinell hardness is designated by the most commonly used test standards (ASTM E10-14 [2] and ISO 6506–1:2005) as HBW (H from hardness, B from brinell and W from the material of the indenter, tungsten (wolfram) carbide). In former standards HB or HBS were used to refer to measurements made with steel indenters.
The Vickers hardness test; The Brinell scale; The Janka hardness test; The Rockwell scale; The Durometer scale; The Barcol scale; The Leeb rebound hardness scale;
ISO 409 Metallic materials — Hardness test — Tables of Vickers hardness values for use in tests made on flat surfaces ISO 409-1:1982 Metallic materials — Hardness test — Tables of Vickers hardness values for use in tests made on flat surfaces — Part 1: HV 5 to HV 100 [Withdrawn: replaced with ISO 6507-1 and ISO 6507-4]
Vickers test scheme An indentation left in case-hardened steel after a Vickers hardness test. The hardness of a material is directly related to its incompressibility, elasticity and resistance to change in shape. A superhard material has high shear modulus, high bulk modulus, and does not deform plastically. Ideally superhard materials should ...
ASTM E140 - 12be1 "Standard Hardness Conversion Tables for Metals Relationship Among Brinell Hardness, Vickers Hardness, Rockwell Hardness, Superficial Hardness, Knoop Hardness, Scleroscope Hardness, and Leeb Hardness" International standards: ISO/DIS 16859-1 "Metallic materials - Leeb hardness test - Part 1: Test method"