A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels .
The Vickers hardness test was developed in 1921 by Robert L. Smith and George E. Sandland at Vickers Ltd as an alternative to the Brinell method to measure the hardness of materials. [1] The Vickers test is often easier to use than other hardness tests since the required calculations are independent of the size of the indenter, and the indenter ...
The Brinell hardness is designated by the most commonly used test standards (ASTM E10-14 [2] and ISO 6506–1:2005) as HBW (H from hardness, B from brinell and W from the material of the indenter, tungsten (wolfram) carbide). In former standards HB or HBS were used to refer to measurements made with steel indenters.
1 Methods of measuring mineral hardness. 2 Other hardness scales. Toggle the table of contents. ... The Vickers hardness test; The Brinell scale; The Janka hardness test;
Mohs hardness [1] Vickers hardness (MPa) [1] Brinell hardness (MPa) [1] Brinell hardness (MPa) [note 1] [2] 3: Li: lithium: 0.6: 5: 4: Be: beryllium: 5.5: 1670: 590 ...
The hardness number is based on the applied force divided by the surface area of the indent itself, giving hardness units in kgf/mm 2. Microindentation hardness testing can be done using Vickers as well as Knoop indenters. For the Vickers test, both the diagonals are measured and the average value is used to compute the Vickers pyramid number.
Vickers test scheme An indentation left in case-hardened steel after a Vickers hardness test. The hardness of a material is directly related to its incompressibility, elasticity and resistance to change in shape. A superhard material has high shear modulus, high bulk modulus, and does not deform plastically. Ideally superhard materials should ...
ISO 409 Metallic materials — Hardness test — Tables of Vickers hardness values for use in tests made on flat surfaces ISO 409-1:1982 Metallic materials — Hardness test — Tables of Vickers hardness values for use in tests made on flat surfaces — Part 1: HV 5 to HV 100 [Withdrawn: replaced with ISO 6507-1 and ISO 6507-4]