A superabsorbent polymer (SAP) (also called slush powder) is a water-absorbing hydrophilic homopolymers or copolymers [1] that can absorb and retain extremely large amounts of a liquid relative to its own mass. [2] Water-absorbing polymers, which are classified as hydrogels when mixed, [3] absorb aqueous solutions through hydrogen bonding with ...
Polyvinyl acetate used further for polyvinyl alcohol is manufactured by radical polymerization in methanol solution. Liquid polybutadienes are made by anionic or radical polymerization in hydrocarbon solutions. Butyl rubber (IIR) by low temperature cationic copolymerization of isobutylene with isoprene in ethylene or methylchloride solution.
It is a common observation that when oil and water are poured into the same container, they separate into two phases or layers, because they are immiscible.In general, aqueous (or water-based) solutions, being polar, are immiscible with non-polar organic solvents (cooking oil, chloroform, toluene, hexane etc.) and form a two-phase system.
Super-absorbent polymers (SAP) similar to sodium polyacrylate were developed in the 1960s by the U.S. Department of Agriculture. [3] Before the development of these substances, the best water absorbing materials were cellulosic or fiber-based like tissue paper, sponge, cotton, or fluff pulp.
In polymer chemistry, suspension polymerization is a heterogeneous radical polymerization process that uses mechanical agitation to mix a monomer or mixture of monomers in a liquid phase, such as water, while the monomers polymerize, forming spheres of polymer. [2] The monomer droplets (size of the order 10-1000 μm) are suspended in the liquid ...
There are two examples each for liquid-liquid and liquid-in-liquid emulsion, either using one monomer or two. The most commonly used interfacial polymerization methods fall into 3 broad types of interfaces: liquid-solid interfaces, liquid-liquid interfaces, and liquid-in-liquid emulsion interfaces. [ 1 ]
A small amount of superabsorbent polymer material is taken (0.1g) and it is placed in the beaker. 100 ml of deionized water is poured into the beaker. After 20 min the swollen polymer was separated by using [filter paper] By weighing the polymer, one can find the swollen capacity of the SAP material. [3]
Polymer solutions are solutions containing dissolved polymers. [1] These may be liquid solutions (e.g. in aqueous solution), or solid solutions (e.g. a substance which has been plasticized). [2] The introduction into the polymer of small amounts of a solvent (plasticizer) reduces the temperature of glass transition, the yield temperature, and ...