Steel with a high carbon content will reach a much harder state than steel with a low carbon content. Likewise, tempering high-carbon steel to a certain temperature will produce steel that is considerably harder than low-carbon steel that is tempered at the same temperature. The amount of time held at the tempering temperature also has an effect.
Holloman and Jaffe determined the value of C experimentally by plotting hardness versus tempering time for a series of tempering temperatures of interest and interpolating the data to obtain the time necessary to yield a number of different hardness values. This work was based on six different heats of plain carbon steels with carbon contents ...
Forging temperature is the temperature at which a metal becomes substantially more soft, ... Carbon steel - 0.50% carbon content 1230 [2] 2246 ~1425-1540
A hypoeutectoid carbon steel (carbon composition smaller than the eutectoid one) is heated to approximately 30 to 50 °C (54 to 90 °F) above the austenictic temperature (A 3), whereas a hypereutectoid steel is heated to a temperature above the eutectoid one (A 1) for a certain number of hours; this ensures all the ferrite transforms into ...
Abrasion resistant steel undergoes a two-step heat treatment process called quenching and tempering, which alters the steel's grain structure to increase hardness and toughness. [ 2 ] During the quenching phase, the steel is heated to an above-critical temperature and is then rapidly cooled with water.
Tempered at 150°C and air cooled 32.2 32.2 32.8 Tempered at 200°C and air cooled 33.1 33.9 33.5 Tempered at 250°C and air cooled 36.8 36.4 37.2 Tempered at 300°C and air cooled 37.7 38.5 38.1 Tempered at 350°C and air cooled 38.1 38.5 38.9 List: Hattori, D., J. Iron Steel Inst. (London) 129 (1), 189–306, 1934 in TPRC I pp 1115–1120 ...
TTT diagram of isothermal transformations of a hypoeutectoid carbon steel; showing the main components obtained when cooling the steel and its relation with the Fe-C phase diagram of carbon steels. Austenite is slightly undercooled when quenched below Eutectoid temperature. When given more time, stable microconstituents can form: ferrite and ...
Austempering is heat treatment that is applied to ferrous metals, most notably steel and ductile iron. In steel it produces a bainite microstructure whereas in cast irons it produces a structure of acicular ferrite and high carbon, stabilized austenite known as ausferrite. It is primarily used to improve mechanical properties or reduce ...